Low-temperature plasma etching of high aspect-ratio densely packed 15 to sub-10 nm silicon features derived from PS-PDMS block copolymer patterns

The combination of block copolymer (BCP) lithography and plasma etching offers a gateway to densely packed sub-10 nm features for advanced nanotechnology. Despite the advances in BCP lithography, plasma pattern transfer remains a major challenge. We use controlled and low substrate temperatures during plasma etching of a chromium hard mask and then the underlying substrate as a route to high aspect ratio sub-10 nm silicon features derived from BCP lithography. Siloxane masks were fabricated using poly(styrene- b -siloxane) (PS-PDMS) BCP to create either line-type masks or, with the addition of low molecular weight PS-OH homopolymer, dot-type masks. Temperature control was essential for preventing mask migration and controlling the etched feature’s shape. Vertical silicon wire features (15 nm with feature-to-feature spacing of 26 nm) were etched with aspect ratios up to 17 : 1; higher aspect ratios were limited by the collapse of nanoscale silicon structures. Sub-10 nm fin st...

Zuwei Liu, Xiaodan Gu, Justin Hwu, Simone Sassolini and Deirdre L Olynick

Click for full article